These balls are martensitic in nature and they have a good corrosion resistance. As a standard practice at the Tolia group all stainless steel balls are supplied in a passivated condition.

Applications :
  • These balls are used in various applications and are used as a cheaper alternative to the AISI 420C material.
Chemical composition
Type %C %Si %Mn %P %S %Cr
420B 0.26-0.35 1.00 max 1.50 max 0.040 max 0.030 max 12.00-14.00
International Standards and material codes
USA GER FRA UK RUS CHN JAP
420B 1.4028 Z 33 C 13 420 S 45 30 Kh 13 3Cr13 420J2
Technical Properties
Property Type U.o.M. Values U.o.M. Values
Hardness Mechanical [HRC] 48 - 58 - -
Ultimate tensile strength Mechanical [MPa] 1700 - 1900 [psix10^3] 250 - 275
Size Range/Grade selection
Product Size Range U.o.M. Grade Capabilities
Balls 3.00 mm to 76.20 mm [mm] GR.20 to GR.2000 as per any international standard.

Comparison Chart- Material Corrosion Resistance

Material

CORROSION RESISTANCE
Air Water Food Liquor Dilute Acid Conc. Acid Chemical
Industrial Atmosphere Salt Air Wet Steam Domestic Water Sea Water Food Product Fruit & Veg. Juice Dairy Product Hot Sulfate Dye HCL H2SO4 HNO3 Phosphoric H2SO4 HNO3 Phosphoric Ammonia Alkaline Salt
AISI-E-52100 3 4 4 2 3
AISI-420 2 4 1 1 3 3 2 3 2 3
AISI 420C 2 4 1 1 3 3 2 3 2 3
AISI 440C 2 3 2 2 2 2 3 4 3 2
AISI 304/302 2 1 1 1 1 1 2 2 1 4 2 2 2 2 😑 2 2 1 1
AISI 316 2 1 1 1 1 1 1 1 2 4 2 1 2 1 1 1 1 2
AISI 1085 3 4 4 2 3

1=Excellent 2 = Good 3 = Fair 4 = Poor

← Will not withstand corrosion

😑 Varies

* = satisfactory only over 75% concentration